MECHANICAL

Value

Unit

Standard

Taber Abrasion, CS-17, 1 kg

65

mg/1000cy

SABIC Method

Tensile Stress, break, 5 mm/min

80

MPa

ISO 527

Tensile Strain, break, 5 mm/min

2

%

ISO 527

Tensile Modulus, 1 mm/min

5500

MPa

ISO 527

Flexural Stress, break, 2 mm/min

125

MPa

ISO 178

Flexural Modulus, 2 mm/min

4500

MPa

ISO 178

Hardness, H358/30

125

MPa

ISO 2039-1

IMPACT

Value

Unit

Standard

Izod Impact, unnotched 80*10*4 +23°C

25

kJ/m²

ISO 180/1U

Izod Impact, unnotched 80*10*4 -30°C

25

kJ/m²

ISO 180/1U

Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm

30

kJ/m²

ISO 179/1eU

Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm

30

kJ/m²

ISO 179/1eU

THERMAL

Value

Unit

Standard

CTE, -40°C to 40°C, flow

5.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

6.8E-05

1/°C

ASTM E 831

Thermal Conductivity

0.28

W/m-°C

ISO 8302

CTE, -40°C to 40°C, flow

5.E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

6.8E-05

1/°C

ISO 11359-2

CTE, 23°C to 80°C, flow

3.E-05

1/°C

ISO 11359-2

CTE, 23°C to 80°C, xflow

7.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 125°C +/- 2°C

PASSES

-

IEC 60695-10-2

Ball Pressure Test, approximate maximum

135

°C

IEC 60695-10-2

Vicat Softening Temp, Rate A/50

150

°C

ISO 306

Vicat Softening Temp, Rate B/50

140

°C

ISO 306

Vicat Softening Temp, Rate B/120

145

°C

ISO 306

HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm

135

°C

ISO 75/Be

HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

130

°C

ISO 75/Ae

Relative Temp Index, Elec

110

°C

UL 746B

Relative Temp Index, Mech w/impact

105

°C

UL 746B

Relative Temp Index, Mech w/o impact

110

°C

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.25

-

ASTM D 792

Mold Shrinkage on Tensile Bar, flow (2) (5)

0.2 - 0.4

%

SABIC Method

Density

1.25

g/cm³

ISO 1183

Water Absorption, (23°C/sat)

0.22

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.07

%

ISO 62

Melt Volume Rate, MVR at 280°C/10.0 kg

12

cm³/10 min

ISO 1133

ELECTRICAL

Value

Unit

Standard

Comparative Tracking Index (UL) {PLC}

3

PLC Code

UL 746A

Volume Resistivity

1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil, 0.8 mm

30

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 1.6 mm

25

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 3.2 mm

16

kV/mm

IEC 60243-1

Relative Permittivity, 1 MHz

2.9

-

IEC 60250

Dissipation Factor, 50/60 Hz

0.004

-

IEC 60250

Dissipation Factor, 1 MHz

0.002

-

IEC 60250

Comparative Tracking Index

225

V

IEC 60112

Relative Permittivity, 50/60 Hz

3

-

IEC 60250

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized, 94V-1 Flame Class Rating (3)

1.5

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating (3)

6

mm

UL 94

UL Recognized, 94-5VA Rating (3)

2

mm

UL 94

Glow Wire Flammability Index 960°C, passes at

3.2

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature, 1.0 mm

800

°C

IEC 60695-2-13

Glow Wire Ignitability Temperature, 2.0 mm

800

°C

IEC 60695-2-13

Oxygen Index (LOI)

30

%

ISO 4589