常用塑料的耐热性能(未经改性的)

热变形温度----------维卡软化点 ------------马丁耐热

HDPE -----------------80-------------------------120 ------------------------\

LDPE-------------------50--------------------------95--------------------------\

EVA---------------------\---------------------------- 64-------------------------\

PP........................102........................110........................\

PS........................85............................105..................... \

PMMA...................100..........................120...................... \

PTFE.....................260..........................110.......................\

ABS.......................86...........................160......................75

PSF.......................185..........................180.....................150

POM.......................98............................141.....................55

PC.........................134.............................153...................112

PA6.......................58..............................180....................48

PA66......................60..............................217................... 50

PA1010..................55..............................159.....................44

PET........................70..............................\........................80

PBT........................66..............................177....................49

PPS........................240.............................\........................102

PPO.......................172..............................\........................110

PI...........................360........................... 300..................... \

LCP........................315..............................\ .........................\

.塑料的增强耐热改性

用增强改性的方法提高塑料的耐热性效果比填充还好,常用的耐热纤维主要有:石棉纤维 玻璃纤维 碳纤维 晶须 聚

1.结晶型树脂经30%玻璃纤维增强耐热改性. PBT的热变形温度由66度提高到210度. PET的热变形温度由98度提高到238度. PP的热变形温度由102度提高到149度. HDPE的热变形温度由49度提高到127度. PA6的热变形温度由70度提高到215度. PA66的热变形温度由71度提高到255度. POM的热变形温度由110度提高到163度. PEEK的热变形温度由230度提高到310度.

2.非结晶树脂经30%玻璃纤维增强耐热改性. PS的热变形温度由93度提高到104度. PC的热变形温度由132度提高到143度. AS的热变形温度由90度提高到105度. ABS的热变形温度由83度提高到110度. PSF的热变形温度由174度提高到182度. MPPO的热变形温度由130度提高到155度.

塑料共混耐热改性

塑料共混提高耐热性即在低热树脂中混入高耐热性树脂从而提高其耐热性. 这种方法虽然耐热性提高幅度不如添加耐热改性高,但其优点是在提高耐 热性同时基本不影响其原有其他性能.如: ABS/PC 热变形温度可由93度提高到125度 ABS/PSF(20%) 热变形温度可达115度

HDPE/PC(20%) 维卡软化点可由124度提高到146度. PP/CaCo3/EP 热变形温度可由102度提高到150度

塑料交联耐热改性

塑料交联提高耐热性常用于耐热管材和电缆方面.如:

1.HDPE经过硅烷交联处理后,其热变形温度可由原来的70度增加到90~110度. 2.PVC经过交联后,其热变形温度可由原来的65度增加到105度