ULTEM™ ATX200 基础创新塑料PEI 物性表/注塑参数

(2014-02-12 14:09:23)
标签:

ultem&trade

atx200

基础创新塑料pei

分类: 塑胶原料
ULTEM™ ATX200 基础创新塑料PEI 物性表:

不透明,具有高冲击强度,水解稳定性,抗污性,阻燃V-0级,ROHS合规,ECO Compliant生态兼容,高流动热混合树脂,适用于餐饮和汽车应用环境,注塑成型.

Tensile Stress, yld, Type I, 5 mm/min

980

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

860

kgf/cm²

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

7

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

70

%

ASTM D 638

Tensile Modulus, 5 mm/min

33600

kgf/cm²

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1470

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

32300

kgf/cm²

ASTM D 790

Taber Abrasion, CS-17, 1 kg

20

mg/1000cy

SABIC Method

Tensile Stress, yield, 50 mm/min

95

MPa

ISO 527

Tensile Stress, break, 50 mm/min

75

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

6.5

%

ISO 527

Tensile Strain, break, 50 mm/min

20

%

ISO 527

Tensile Modulus, 1 mm/min

3000

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

125

MPa

ISO 178

Flexural Modulus, 2 mm/min

3100

MPa

ISO 178

Hardness, H358/30

125

MPa

ISO 2039-1

IMPACT

Value

Unit

Standard

Izod Impact, unnotched, 23°C

212

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

5

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

5

cm-kgf/cm

ASTM D 256

Izod Impact, Reverse Notched, 3.2 mm

272

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

509

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*4 +23°C

5

kJ/m²

ISO 180/1A

Izod Impact, notched 80*10*4 -30°C

5

kJ/m²

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm

4

kJ/m²

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm

4

kJ/m²

ISO 179/1eA

THERMAL

Value

Unit

Standard

Vicat Softening Temp, Rate B/50

209

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

187

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

191

°C

ASTM D 648

CTE, -40°C to 150°C, flow

5.E-05

1/°C

ASTM E 831

CTE, -40°C to 150°C, xflow

5.E-05

1/°C

ASTM E 831

Thermal Conductivity

0.23

W/m-°C

ISO 8302

CTE, 23°C to 150°C, flow

5.E-05

1/°C

ISO 11359-2

CTE, 23°C to 150°C, xflow

5.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 125°C +/- 2°C

PASSES

-

IEC 60695-10-2

Vicat Softening Temp, Rate A/50

210

°C

ISO 306

Vicat Softening Temp, Rate B/50

200

°C

ISO 306

Vicat Softening Temp, Rate B/120

205

°C

ISO 306

HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm

195

°C

ISO 75/Be

HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

180

°C

ISO 75/Ae

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.26

-

ASTM D 792

Mold Shrinkage on Tensile Bar, flow (2) (5)

0.5 - 0.7

%

SABIC Method

Mold Shrinkage, flow, 3.2 mm (5)

0.5 - 0.7

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm (5)

0.5 - 0.7

%

SABIC Method

Melt Flow Rate, 337°C/6.6 kgf

24

g/10 min

ASTM D 1238

Density

1.26

g/cm³

ISO 1183

Water Absorption, (23°C/sat)

0.9

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.5

%

ISO 62

Melt Volume Rate, MVR at 340°C/5.0 kg

16

cm³/10 min

ISO 1133

ELECTRICAL

Value

Unit

Standard

Hot Wire Ignition {PLC)

0

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC}

4

PLC Code

UL 746A

Volume Resistivity

1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Relative Permittivity, 1 MHz

2.9

-

IEC 60250

Dissipation Factor, 50/60 Hz

0.001

-

IEC 60250

Dissipation Factor, 1 MHz

0.005

-

IEC 60250

Comparative Tracking Index

150

V

IEC 60112

Relative Permittivity, 50/60 Hz

2.9

-

IEC 60250

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized, 94V-2 Flame Class Rating (3)

0.75

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating (3)

1.5

mm

UL 94

 

ULTEM™ ATX200 PEI SABIC基础创新塑料 注塑成型参数:

Drying Temperature 130 to 140 °C
Drying Time 3.0 to 4.0 hr
Hopper Temperature 80.0 to 100 °C
Rear Temperature 320 to 340 °C
Middle Temperature 330 to 350 °C
Front Temperature 340 to 360 °C
Nozzle Temperature 340 to 360 °C
Processing (Melt) Temp 340 to 380 °C
Mold Temperature 125 to 140 °C

ULTEM™ <wbr>ATX200 <wbr>基础创新塑料PEI <wbr>物性表/注塑参数

PEI原料物性描述:
(1)PEI的特点是在高温不具有高的强度、高的刚性、耐磨性和尺寸稳定性。
(2)PEI是琥珀色透明固体,不添加任何添加剂就有固有的阻燃性和低烟度,氧指数为47%
燃烧等级为UL94-V-0级。
(3)PEI的密度为1.28~1.42g/cm3,玻璃化温度为215℃,热变形温度198~208℃,可在160~
180℃下长期使用,允许间歇最高使用温度为200℃
(4)PEI具有优良的机械强度、电绝缘性能、耐辐射性、耐高低温及耐疲劳性能和成型加
工性;加入玻璃纤维、碳纤维或其他填料可达到增强改性目的。
(5)PEI的化学结构是在芳香族亚酰胺和醚的单元重复基础上组成的,对众多化学品都稳
定,如绝大多数烃类、醇类、全卤代溶剂,溶于特殊的卤代溶剂。

0

阅读 评论 收藏 禁止转载 喜欢 打印举报/Report